《塑料及树脂缩写中英文对照表51121(28页).doc》由会员分享，可在线阅读，更多相关《塑料及树脂缩写中英文对照表51121(28页).doc（28页珍藏版）》请在taowenge.com淘文阁网|工程机械CAD图纸|机械工程制图|CAD装配图下载|SolidWorks_CaTia_CAD_UG_PROE_设计图分享下载上搜索。
1、-塑料及树脂缩写中英文对照表51121缩写代号中文化学名英文名Top of FormAAS丙烯腈、丙烯酸酯、苯乙烯共聚物Acrylnitril-Acrylicester-Styrene CopolymerABR丙烯酸酯-丁二烯橡胶 （参见AR）Acrylester-Butadiene Rubber(ASTM)ABS丙烯腈-丁二烯-苯乙烯共聚物Acrylonitrile-butadiene-styrene copolymerA/S丙烯腈苯乙烯共聚物Acrylonitrile-styrene copolymerACM丙烯酸酯-2-氯乙烯醚橡胶(参见AR)Acrylester-2-Chlorovin
2、ylether rubber(ASTM)ACS苯乙烯、丙烯腈与氯化聚乙烯混合物SAN blend with chlorinated polyethyleneAFMU亚硝基橡胶;三氟亚硝基甲烷、亚硝基全氟丁酸Nitrosorubber;TerpolymersofTFE,Trifluoronitrosomethane and Nitrosoperfluorobutyric acid(ASTM)AL藻朊酸纤维Alginate FibersALK醇酸树脂Alkyd ResinA/MMA丙烯腈-甲基丙烯酸酯共聚物Acrylonitrile-metry1 methacrylate copolymerANM
3、丙烯酸酯丙烯腈橡胶(参见AR)Acrylester-Acrylnitril Rubber(ASTM)AP乙丙橡胶(参见APK,EPM,EPR)Ethylene-Propylene RubberAPK乙丙橡胶(参见AP,APT,EPM,EPR)Ethylene-Propylene RubberAPT三元乙丙橡胶(参见EPDM,EPT,EPTR)Ethylene-Propylene Terpolymerisate RubberAR丙烯酸酯橡胶(参见ABR,ACM,ANM)Acrylester Rubber(BS)A/S/A丙烯腈-苯乙烯-丙烯酸酯共聚物Acrylonitrile-styrene-a
4、crylate copolymerBBP邻苯二酸丁酯苯酯Benzyl Butyl Phthalate(DIN,ISO)BOA已二酸辛酯苄酯Benzyl Octyl Adipate(ISO)BMC块状模塑料Bulk Moulding CompoundBR聚丁二烯橡胶Polybutadiene Rubber(ASTM)Buty1丁基橡胶(参见IIR,PIBI)Buty1 Rubber(BS)CA乙酸纤维素Cellulose acetateCAB乙酸-丁酸纤维素Cellulose acetate butyrateTop of FormCAP乙酸-丙酸纤维素Cellulose acetate prop
5、ionateCF甲酚-甲醛树脂Cresol-formaldehyde resinCFK化纤增强塑料(参见KFK)Chemical Fiber Reinforced PlasticsCFM聚三氟氯乙烯(参见PCTFE)Polychloro-Trifluoro Ethylene(ASTM)CFRP碳纤维增强塑料Carbon Fiber Reinorced PlasticsCHC共聚氯醇乙烯化氧橡胶(参见CHR,CO,ECO)Epichlorohydrin Ethylenoxide RubberBottom of FormCHR均聚氯醇橡胶(参见CHC,CO,ECO)Epichlorohydrin
6、RubberCM氯化聚乙烯(参见CPE)Chlorinated Polyethyene(ASTM)CMC羧甲基纤维素Carboxymethyl celluloseCN硝酸纤维素Cellulose nitrateCP丙酸纤维素Cellulose propiomateCS酷素塑料Casein plasticsCT三醋酸纤维Triacetate FiberCTA三乙酸纤维素Cellulose Triacetate(GB)CTA三乙酸纤维素Cellulose triacetateDABCO三乙撑二胺Triethylene DiamineDAP苯二酸二烯丙酯树脂(参见FDAP)Diallyl Phtha
7、late Resin(DIN,ASTM)DBP邻苯二（甲）酸二丁酯Dibutyl Phthalate(DIN,ISO,IUPAC)DCP邻苯二酸辛酯Dicapryl Phthalate(DIN,ISO,IUPAC)DDP邻苯二酸二癸酯Didecyl Phthalate(DIN,ISO,IUPAC)DEP邻苯二酸二乙酯Diethyl Phthalate(ISO)DHP邻苯二酸二庚酯Diheptyl Phthalate(ISO)DHXP邻苯二酸二已酯Dihexyl Phthalate(ISO)DIBP邻苯二酸二异丁酯Diisobutyl Phthalate(DIN,ISO)DIDA已二酸二异类癸酯
8、Diisodecyl Adipate(DIN,ISO,IUPAC)DIDP邻苯二酸二异癸酯Diisodecyl Phthalate(DIN,ISO,IUPAC)DINA已二酸二异壬酯Diisononyl Adipate(ISO)DINP邻苯二酸二异壬酯Diisononyl Phthalate(DIN,ISO)DIOA已二酸二异辛酯Diisooctyl Adipate(DIN,ISO,IUPAC)DIOP邻苯二酸二异辛酯Diisooctyl Phthalate(DIN,ISO,IUPAC)DIPP邻苯二酸二异戊酯Diisopentyl PhthalateDITDP邻苯二酯二异十三酯Diisotr
9、idecyl P(DIN,ISO)DITP邻苯二酯二异十三酯(参见DITDP)Diisotridecyl Phthalate(DIN)DMC面团模塑料Dough Molding CompoundDMF二甲基甲酰胺Dimethyl FormamideDMP邻苯二酸二甲酯Dimethyl Phthalate(ISO)DMT对苯二酯二甲酯Dimethyl TerephthalateDNP邻苯二酸二壬酯Dinonyl Phthalate(ISO,IUPAC)DOA已二酯二辛酯，已二酸二（2-乙已基）酯Dioctyl Adipate,Di-2-Ethyexyl Adipate(DIN,ISO,IUPAC
10、)DODP邻苯二酸辛、癸酯(参见ODP)Dioctyl Decyl Phthalate(ISO)DOIP间苯二酸二辛酯，间苯二酸二（2-乙已基）酯Dioctyl Isophthalate,Di-2-Ethylhexyl Isophthalate(DIN,ISO)DOP邻苯二酸二辛酯，邻苯二酯二（2-乙已基）酯Dioctyl Phthalate Di-2-Ethylhexyl Phthalate(DIN,ISO,IUPAC)DOS癸二酸二辛酯，癸二酸二（2-乙已基）酯Dioctyl Sebacate,Di-2-Ethylhexyl Sebacate(DIN,ISO,IUPAC)DOTP对苯二酸二
11、辛酯，对苯二酸二（2-乙已基）酯Dioctyl Terephthalate,Di-2-Ethylhexyl Terephthalate(DIN,ISO)DOZ壬二酸二辛酯，壬二酸二（2-乙已基）酯Dioctyl Azelate,Di-2-Ethylhexyl Azelate(DIN,ISO,IUPAC)DPCF磷酸二苯甲苯酯Diphenyl Cresyl Phosphate(ISO)DPOF磷酸二苯辛酯Diphenyl Octyl Phosphate(ISO)DUP苯二酸十一烷酯Diundecyl PhthalateEC乙基纤维素Ethyl celluloseECB乙烯共聚体与沥青混合物Eth
12、ylene Copolymer Bitumen MixtureECO氯醇橡胶(参见CHC,CHR,CO)Epichlorohydrin Rubber(ASTM)EEA乙烯/丙烯酸乙酯共聚物Ethylene Ethylacrylate Copolymer(ISO)ELO环氧化亚麻仁油Epoxydized Linseed Oil(DIN,ISO)EP环氧树脂Epoxide resinE/P乙烯-丙烯共聚物Ethylene-propylene copolymerE/P/D乙烯-丙烯-二烯三元共聚物Ethylene-tetrafluoroethylene copolymerE/TFE乙烯-四氟乙烯共聚
13、物Ethhlene-tetrafluoroethylene copolymerE/VAC乙烯-乙酸乙烯酯共聚物Ethylene-vinylacetate copolymerE/VAL乙烯-乙烯醇共聚物Ethylene-vinylalcohol copolymerFDAP苯二酸二烯丙酯（树脂）(参见DAP)Diallyl Phthalate(Resin)FEP全氟（乙烯-丙烯）共聚物，四氟乙烯-六氟丙烯共聚物Perfluorinated ethvlence-propylene copolymerFLU维通橡胶VitonFPM偏氟乙烯/六氟丙烯橡胶Vinylidene Fluoride Hexaf
14、lyoropropylene Rubber(ASTM)FRP纤维增强塑料Fiber Reinforce PlasticsFSI含氟甲基硅烷橡胶Fluoro Methylsilicon Rubber(ASTM)GPS通用聚苯乙烯General polystyeneGRP玻璃纤维增强塑料Glass fibre reinforced plasticsHDPE高密度聚乙烯High density polyethyleneHIPS高冲击强度聚苯乙烯High impact polyethyleneHMWPE高分子量聚乙烯High Molecular Weight PolyethyleneHR丁基橡胶(参见
15、Butyl,PIBI)Brtyl Rubber,Isprene Isobutylene Copolymer(ASTM)IR异戊二烯橡胶Isoprene Rubber,Cis 1,4-Polyisoprene Synthetic Natural Rubber(ASTM,BS)KFK碳纤维增强塑料Carbonfiber Reinforced Plastics(DIN)LDPE底密度聚乙烯Low density polyethyleneMBS甲基丙烯酸甲酯/丁二烯/苯乙烯共聚物Methyl Methacrylate Butadiene Styrene CopolymerMC甲基纤维素Methyl c
16、elluloseMDPE中密度聚乙烯Middle density polyethyleneMF三聚氰胺-甲醛树脂Melamine- formaldehyde resinMPF三聚氰胺-酚甲醛树脂Melamine-phenlo-formaldehyde resinNBR丁腈橡胶(参见PBAN)Butadiene Acrylnitrile Rubber,Nitrile Rubber(ASTM,BS)NC硝基纤维素(参见CN)NitrocelluloseNCR腈基氯丁橡胶Nitrile Chloroprene Rubber(ASTM)NDPE低压法聚乙烯Low Pressure Polyethyle
17、neNK,NR天然橡胶Natural Rubber(ASTM)ODP苯二酸辛、癸酯(参见DODP)Octyl Decyl Phthalate(ISO)OER油充橡胶Oil Extended RubberPA聚酰胺PolyamidePA4尼龙4，聚丁内酰胺及纤维Pa from ButyrolactamPA6尼龙6，聚已内酰胺及纤维Pa from Caprolactam(DIN,ISO)PA6I尼龙6I，间苯二酯六甲基二胺及纤维Pa from Hexamethylene Diamine and IsophthalacidPA6T尼龙6T，聚对苯二甲酰已二胺及纤维Pa from Hexamethyl
18、enediamine and TerephthalicacidPA66尼龙66，聚已二酰已二胺及纤维PA from Hexamothylene diamine and Adipic acidPA610尼龙610，聚癸二酸已二胺及纤维PA from Hexamethylene diamine and Sebacic acid(DIN,ISO)PA1010尼龙1010，聚癸二栈癸二胺及纤维PA from Sebacicdiamine and Sebacic acidPA11尼龙11，聚氨基十一酸及纤维PA from 11 amine-Undeca acid(DIN,ISO)PA12尼龙12，聚十二
19、内酰胺及纤维PA from Lauric Lactam(DIN,ISO)PA6/12尼龙612，聚已内酰胺和聚十二内酰胺混合物及纤维Mixed PA from Caprolactam and Dcdecanlactam(DIN,ISO)PA66/610尼龙66/610及纤维Mixed PA from Hexamethylene diamine Adipic acid and Sebacic acidPAA聚丙烯酸Poly(acrylic acid)PAC聚丙烯腈及纤维(参见PAN,PC)Polyacrylonitrile(IUPAC)PAN聚丙烯腈PolyacrylonitrilePB聚丁烯-
20、1Polybutene-1PBTP聚对苯二甲酸丁二（醇）酯Poly (butylenes terephthalate)PC聚碳酸酯PolycarbonatePCR氯丁橡胶Polychloroprene RubberPCTFE聚三氟氯乙烯PolychlorotrifluoroethylenePDAP聚邻苯二甲酸二烯丙酯Poly(diallyl phthalate)PDAIP聚间苯二甲酸二烯丙酯Poly(diallyl isophthalate)PE聚乙烯PolyethylenePEC氯化聚乙烯Chlorinated polyethylenePeCe氯化聚氯乙烯及纤维(参见CPVC,PC,PVCC
21、)After Chlorinated PVCPEOX聚氧化乙烯；聚环氧乙烷Poly(ethylene oxide)PETP聚对苯二甲酸乙二（醇）酯Poly(ethylene terephthalate)PF酚醛树酯Phenol-formaldehyde resinPFEP四氟乙烯/六氟丙烯共聚物(参见FEP)Tetrafluoroethylene Hexafluoropropylene CopolymerPI聚酰亚胺PolyimidePMCA聚a-氯化丙烯酸甲酯Poly(methyl-a-chloroacrylate)PIB聚异丁烯Polyisobutylene(DIN,BS)PIBI丁基橡胶
22、(参见Butyl,IIR)Butyl Rubber,Isoprene Isobutene RubberPMI聚甲基丙烯酰亚胺PolymethacrylimidePOM聚甲醛polyformaldehyde(polyoxymethylene)PMMA聚甲基丙烯酸甲酯Poly(methyl methacrylate)POR环氧丙浣橡胶Polyepoxy RubberPP聚丙烯PolypropylenePPC氯化聚丙烯Chlorinated polypropylenePPO聚苯醚（聚2，6-二甲基苯醚），聚苯撑氧Poly(phenylene oxide)PPOX聚氧化丙烯，聚环氧丙烷Poly(pro
23、pylene oxide)PPS聚苯硫醚Poly(phenylene sulfide)PPSU聚苯砜Poly(phenylene sulfone)PS聚苯乙烯PolystyrenePSAN苯乙烯/丙烯腈共聚物(参见SAN)Styrene Acrylnitrile Copolymer(DIN)PSB苯乙烯/丁二烯共聚物(参见SB)Styrene Butadiene Copolymer(DIN)PSI甲基苯基硅橡胶Methylsilicone Rubber With Phonyl Group(ASTM)PSU聚砜PolysulfonePTFE聚四氟乙烯Polytetrafluoroethylene
24、PUR聚氨酯polyurethanePVAC聚乙酸乙烯酯polyurethanePVAL聚乙烯醇Poly(vinyl alcohol)PVB聚乙烯醇缩丁醛Poly(vinylbutyral)PVC聚氯乙烯Poly(vinyl chloride)PVA聚乙烯醇及纤维(参见PVAC)PolyvinylalcoholPVAA聚乙烯醇缩醛纤维Polyvinyl AcetalPVCA氯乙烯-乙酸乙烯酯共聚物Poly(vinyl chloride-acetate)PVCC氯化聚氯乙烯Chlorinated poly(vinyl chloride)PVDC聚偏二氯乙烯Poly(vinylidene chlo
25、ride)PVDF聚偏二氟乙烯Poly(vinylidene fluorde)PVF聚氟乙烯Poly(vinyl fluoride)PVF2聚偏二氟乙烯(参见PVDF)Polyvinylidene FluoridePVFM聚乙烯醇缩甲醛Poly(vinyl formal)PVK聚乙烯基咔唑Poly(vinyl carbazole)PVFO聚乙烯醇缩甲醛(参见PVFM)Polyvinylformal(DIN)PVSI甲基苯基乙烯基硅橡胶Methylsilicone Rubber with Phenyl and Vinyl Group(ASTM)PVP聚乙烯基吡咯烷酮Poly(vinyl pyrr
26、olidone)PVSI甲基苯基乙烯基硅橡胶Methylsilicone Rubber with Phenyl and Vinyl Group(ASTM)PY不饱和聚酯树脂Unsaturated Polyester Resin(BS)RP增强塑料Reinforced plasticsRF间苯二酚-甲醛树脂Resoreinol-formaldehyde resinS/AN苯乙烯-丙烯腈共聚物Styrene-acrylonitrile copolymerSAN苯乙烯/丙烯腈共聚物(参见PSAN)Styrene-Acrylnitrile Copolymer(GB,DIN,ISO)SB苯乙烯/丁二烯(
27、参见PSB)Styrene-Butadiene(DIN,ISO)SBR丁苯橡胶Styrene Butadiene Rubber(ASTM,BS)SBS苯乙烯/丁二烯/苯乙烯嵌段共聚物Styrene Butadiene Styrene block PolymerSCR苯乙烯氯丁二烯橡胶Styrene Chloroprene Rubber(ASTM)SI聚硅氧烷siliconeS/MS苯乙烯甲基苯乙烯共聚物Styrene-a-methy styrene copolymerS-PVC悬浮聚合聚氯乙烯PVC Suspension PolymerizedSYN合成纤维类Synthetic FibersT
28、CEF磷酸三氯乙酯Tricresyl phosphate(ISO)TCF磷酸三甲苯酯(参见TCP,TKP,TTP)Tricresyl phosphate(DIN,ISO)TCP磷酸三甲苯酯(参见TCP,TKP,TTP)Tricresyl phosphate(IUPAC)TDI甲代苯撑异氰酸酯Toluylene DiisocyanateTIOTM偏苯三酸三异辛酯Triisooctyl Trimellitate(DIN,ISO)TKP磷酸三甲苯酯(参见TCF,TCP,TTP)Tricresyl phosphateTM聚硫橡胶Polysulfide RubbersTMC聚酯粘稠模塑料Thick Mo
29、lding CompoundTOF磷酸三辛酯，磷酸三（2-乙已基）酯(参见TOP)Triocty Phosphate,Tri-2-Ethylhexyl Phosphate(DIN,ISO)TOP磷酸三辛酯(参见TOF)Trioctyl Phosphate(IUPAC)TOPM均苯四甲酸四辛酯Tetraoctyl Pyromellitate(DIN,ISO)TOTM偏笨三酸三辛酯Trioctyl Trimellitate(DIN,ISO)TPA1,5-反式聚戊烯橡胶(参见TPR)1,5-Trans Polypentene RubberTPE热塑性弹性体Thermoplastic Elastome
30、r (TPE)TPF磷酸三酚酯(参见TPP)Triphenyl Phosphate(DIN,ISO)TPP醚酸三酚酯(参见TPF)Triphenyl Phosphate(IUPAC)TPR1.1,5-反式聚戊烯橡胶(参见TPA)1,5-Trans Polypentene Rubber2.热塑性橡胶(参见TR)Thermoplastic RubberTR热塑性橡胶Thermoplastic Rubber丁苯嵌段共聚物(参见TPR)Butadiene Styrene Block CopolymerTTP磷酸三甲苯酯(参见TCF,TCP,TKP)Tricresyl PhosphateUF脲甲醛树脂U
31、rea-formaldehyde resinUHMWPE超高分子量聚乙烯Ultra-high mojecular weight polyethyleneUP不饱和聚酯Unsaturated polyesterUP-G-G玻纤织物聚酯预浸渍物Polyester prepregnated Glassfiber TexfileUP-G-M玻璃毡聚酯预浸渍物Polyester Textilglass Mat PrepregUP-G-R玻璃束聚酯预浸渍物Polyester Textilglass Roving PrepregUR聚氨酯橡胶Polyurethane Rubber(BS)UA醋酸乙烯Viny
32、l AcetateVAC醋酸乙烯Vinyl AcetateVC氯乙烯(参见VCM)VinylchlorideVC/E氯乙烯-乙烯共聚物Vinylchloride-ethylene copolymerVC/E/MA氯乙烯-乙烯-丙烯酸甲酯共聚物Vinylchloride-ethylene-methylacrylate copomerVC/E/VAC氯乙烯-乙烯-乙酸乙烯酯共聚物Vinylchloride-ethylene-vinylacetate copolymerVC/MA氯乙烯-丙烯酸甲酯共聚物Vinylchloride-methylacrylate copolymerVC/MMA氯乙烯-甲
33、基丙烯酸甲酯共聚物Vinylchloride-methyl methylac-rylate copolymerVC/OA氯乙烯-丙烯酸辛酯共聚物Vinylchloride-octylacrylate copolymerVC/VAC氯乙烯-乙酸乙烯酯共聚物Vihylchloride-vinylacetate copolymerVC/VDC氯乙烯-偏二氯乙烯共聚物Vihylchloride-vinylidene chloride copolymerVF硬化纸板Vulcanized FiberVPF交联聚乙烯Crosslinked PolyethyleneVSI甲基乙烯基硅橡胶Methylsilic
34、one Rubber with Vinyl Group(ASTM)WMll增塑剂PlasticizerBottom of Form塑料的定义塑料是指以树脂（或在加工过程中用单体直接聚合）为主要成分，以增塑剂、填充剂、润滑剂，着色剂等添加剂为辅助成分，在加工过程中能流动成型的材料。塑料主要有以下特性：大多数塑料质轻，化学稳定性好，不会锈蚀；耐冲击性好；具有较好的透明性和耐磨耗性；绝缘性好，导热性低；一般成型性、着色性好，加工成本低；大部分塑料耐热性差，热膨胀率大，易燃烧；尺寸稳定性差，容易变形；多数塑料耐低温性差，低温下变脆；容易老化；某些塑料易溶于溶剂。聚苯硫醚（PPS)性能介绍耐热性能优异：
35、其熔点超过280，热变形温度超过260，长期使用温度为220-240。在空气中于700降解在1000惰性气体仍保持40%的重量，短期耐热性和长期连续使用的热稳定性均优于目前所有的工程塑料。经特殊改性的品种，热变形温度可达350以上。自身具有阻燃性：聚苯硫醚阻燃性可达到UL94-0级，氧指数(LOI)57%。 聚苯硫醚自身的化学结构使其具有良好的难燃烧性能，无需加入阻燃剂。机械性能好：其刚性极强，表面硬度高，洛氏硬度100HR,拉伸强度170 MPa ，弯曲强度220MPa，缺口冲击强度16 MPa，弯曲模量3.5104，并具有优异的耐蠕变性和耐疲劳性。耐化学药物性能优异：目前尚未发现可在200
36、以下溶解聚苯硫醚的溶剂，对无机酸、碱和盐类的抵抗性极强。尺寸稳定性好：成型收缩率很低，小于0.0025%，吸收率小于0.05%，线性热膨胀系数也小。在高温、高湿条件下仍表现出良好的尺寸稳定性。故在机械、化工、仪器、仪表和航空、航天、舰船等各个方面都具有广泛用途。电性能优：聚苯硫醚在高温、高湿、高频条件下仍具有优良的电性能，其体积电阻率为11016.cm，表面电阻率为11015，电气强度18KV/mm.耐磨性突出：通过填充氟树脂和碳纤维等润滑剂，可大幅度提高其耐磨性，摩擦系数在0.01-0.02。耐幅射：耐幅射达到Gy 1108，是其它工程塑料无法比拟的新材料，是电子、电气、机械、仪器、航空、航
37、天、军事等领域特别是原子弹、中子弹耐辐射唯一理想的优良材料。加工性能好：PPS树脂的熔体粘度低，流动性好，极易与玻纤润湿接触，因此填充填料容易，用其制备的玻纤或无机填料增强注塑级粒料，具有极高抗伸缩性，抗冲击性，抗弯曲及延展性。在其熔点以上可以统一成形。与金属和非金属粘接性能好：PPS特别对玻璃、铝、钛、不锈钢等具有非常高的粘结强度，附着力达到1级。对玻璃的粘结性能好，极宜作化工设备的衬里。 聚对苯二甲酸丁二醇酯（PBT）聚对苯二甲酸丁二醇酯，英文名polybutyleceterephthalate（简称PBT），PBT为乳白色半透明到不透明、结晶型热塑性聚酯。具有高耐热性、韧性、耐疲劳性，自
38、润滑、低摩擦系数，耐候性、吸水率低，仅为0.1%，在潮湿环境中仍保持各种物性（包括电性能），电绝缘性，但体积电阻、介电损耗大。耐热水、碱类、酸类、油类、但易受卤化烃侵蚀，耐水解性差，低温下可迅速结晶，成型性良好。缺点是缺口冲击强度低，成型收缩率大。故大部分采用玻璃纤维增强或无机填充改性，其拉伸强度、弯曲强度可提高一倍以上，热变形温度也大幅提高。可以在140下长期工作，玻纤增强后制品纵、横向收缩率不一致，易使制品发生翘曲。PBT结晶速度快，最适宜加工方法为注塑，其他方法还有挤出、吹塑、涂覆和各种二次加工成型，成型前需预干燥，水分含量要降至0.02%。PBT（增强、改性PBT）主要用于汽车、电子电
39、器、工业机械和聚合物合金、共混工业。如作为汽车中的分配器、车体部件、点火器线圈骨架、绝缘盖、排气系统零部件、摩托车点火器、电子电器工业中如电视机的偏转线圈，显象管和电位器支架，伴音输出变压器骨架，适配器骨架，开关接插件、电风扇、电冰箱、洗衣机电机端盖、轴套。另外还有运输机械零件，缝纫机和纺织机械零件、钟表外壳、镜筒、电熨斗罩、水银灯罩、烘烤炉部件、电动工具零件、屏蔽套等。已商品化PBT合金有：PBT/弹性体、PBT/PC/弹性体、PBT/PPO、PBT/PE、PBT/ASA合金等。聚碳酸酯(PC)介绍聚碳酸酯是分子主链中含有O-R-O-CO链节的热塑性树脂，按分子结构中所带酯基不同可分为脂肪族
40、、脂环族、脂肪一芳香族型，其中具有实用价值的是芳香族聚碳酸酯，并以双酚A型聚碳酸酯为最重要，分子量通常为3-10万。聚碳酸酯，英文名Polycarbonate,简称PC。PC是一种无定型、无臭、无毒、高度透明的无色或微黄色热塑性工程塑料，具有优良的物理机械性能，尤其是耐冲击性优异，拉伸强度、弯曲强度、压缩强度高；蠕变性小，尺寸稳定；具有良好的耐热性和耐低温性，在较宽的温度范围内具有稳定的力学性能，尺寸稳定性，电性能和阻燃性，可在-60120下长期使用；无明显熔点，在220-230呈熔融状态；由于分子链刚性大，树脂熔体粘度大；吸水率小，收缩率小，尺寸精度高，尺寸稳定性好，薄膜透气性小；属自熄性材
41、料；对光稳定，但不耐紫外光，耐候性好；耐油、耐酸、不耐强碱、氧化性酸及胺、酮类，溶于氯化烃类和芳香族溶剂，长期在水中易引起水解和开裂，缺点是因抗疲劳强度差，容易产生应力开裂，抗溶剂性差，耐磨性欠佳。PC可注塑、挤出、模压、吹塑、热成型、印刷、粘接、涂覆和机加工，最重要的加工方法是注塑。成型之前必须预干燥，水分含量应低于0.02%，微量水份在高温下加工会使制品产生白浊色泽，银丝和气泡，PC在室温下具有相当大的强迫高弹形变能力。冲击韧性高，因此可进行冷压，冷拉，冷辊压等冷成型加工。挤出用PC分子量应大于3万，要采用渐变压缩型螺杆，长径比1：1824，压缩比1：2.5，可采用挤出吹塑，注-吹、注-拉
42、-吹法成型高质量，高透明瓶子。PC合金种类繁多，改进PC熔体粘度大（加工性）和制品易应力开裂等缺陷，PC与不同聚合物形成合金或共混物，提高材料性能。具体有PC/ABS合金，PC/ASA合金、PC/PBT合金、PC/PET合金、PC/PET/弹性体共混物、PC/MBS共混物、PC/PTFE合金、PC/PA合金等，利有两种材料性能优点，并降低成本，如PC/ABS合金中，PC主要贡献高耐热性，较好的韧性和冲击强度，高强度、阻燃性，ABS则能改进可成型性，表观质量，降低密度。PC的三大应用领域是玻璃装配业、汽车工业和电子、电器工业，其次还有工业机械零件、光盘、包装、计算机等办公室设备、医疗及保健、薄膜
43、、休闲和防护器材等。PC可用作门窗玻璃，PC层压板广泛用于银行、使馆、拘留所和公共场所的防护窗，用于飞机舱罩，照明设备、工业安全档板和防弹玻璃。PC板可做各种标牌，如汽油泵表盘、汽车仪表板、货栈及露天商业标牌、点式滑动指示器，PC树脂用于汽车照相系统，仪表盘系统和内装饰系统，用作前灯罩，带加强筋汽车前后档板，反光镜框，门框套、操作杆护套、阻流板、PC被应用用作接线盒、插座、插头及套管、垫片、电视转换装置，电话线路支架下通讯电缆的连接件，电闸盒、电话总机、配电盘元件，继电器外壳，PC可做低载荷零件，用于家用电器马达、真空吸尘器，洗头器、咖啡机、烤面包机、动力工具的手柄，各种齿轮、蜗轮、轴套、导规
44、、冰箱内搁架。PC是光盘储存介质理想的材料。PC瓶（容器）透明、重量轻、抗冲性好，耐一定的高温和腐蚀溶液洗涤，作为可回收利用瓶（容器）。PC及PC合金可做计算机架，外壳及辅机，打印机零件。改性PC耐高能辐射杀菌，耐蒸煮和烘烤消毒，可用于采血标本器具，血液充氧器，外科手术器械，肾透析器等，PC可做头盔和安全帽，防护面罩，墨镜和运动护眼罩。PC薄膜广泛用于印刷图表，医药包装，膜式换向器。聚甲醛(POM)介绍又名聚氧化次甲基，英文名polyoxymethylene（简称POM）。分子结构规整和结晶性使其物理机械性能十分优异，有金属塑料之称。POM为乳白色不透明结晶性线性热塑性树脂，具有良好的综合性能和着色性，具有较高的弹性模量，很高的刚性和硬度，比强度和比刚性接近于金属；拉伸强度，弯曲强度，耐蠕变性和耐疲劳性优异，耐反复冲击，去载回复性优；摩擦系数小，耐磨耗，尺寸稳定性好，表面光泽好，有较高的粘弹性，电绝缘性优，且不受温度影响；耐绝缘性好且不受湿度影响；耐化学药品性优：除了强酸、酚类和有机卤化物外，对其他化学品稳定